- Suitable for all precious metals (including silver).
- A superior ready made flux powder, keeps joints cleaner with less fire stain than borax.
- Mix with water.
- Supplied in a 250g tub.
Clean and degrease the joint surfaces before applying flux. Flux powder should be mixed with water and a few drops of liquid detergent to form a thick paste. Paste should then be brushed onto the joint surfaces before assembly. Further flux should then be applied externally on either side of the joint mouth. Hot Rodding is where a warm brazing rod is dipped into flux powder and the flux adhering to the rod is transferred to the joint area. This is an effective fluxing method but difficult to achieve good penetration of capillary joints. It can be used to supplement a pre-fluxed area during heating.
It is good practice to mechanically clean and degrease the joint surface before applying flux. Heat slowly and evenly to the brazing temperature, without local overheating. Use the flux as a temperature guide - it will become clear or opaque as the brazing temperature is approached. If blackening of the flux occurs this is often a sign of insufficient flux, overheating or flux exhaustion.
The flux residues left after completion of the brazing operation are corrosive and should be removed. The residues for Easy-Flo Flux Powder can easily be removed by soaking in hot water > 40°C for between 15 and 30 minutes. Any remaining residues can then be brushed off in running water.